Criterial parametrs for estimation of polymer solutions for electrospinning of fibers

The possibility of estimating the high-elasticity state of solutions of polymers and oligomers by criterial parameters and dependencies was studied. It was found that the high elasticity of polymer solutions facilitates fiber formation in electroforming. The criteria used are dimensionless values of reduced viscosity and of reduced concentration, as well as the number of nodes in the physical entanglement of the macromolecules .

электроформование, поли-N-винилпирролидон, фенолформальдегидные олигомеры, растворы полимеров, характеристическая вязкость, вязкость, молекулярная масса, полимерные волокна, electrospinning, poly(N-vinyl pyrrolidone), phenol-formaldehyde oligomers, polymer solutions, intrinsic viscosity, viscosity, molecular weight, polymer fibers

1. Филатов Ю.Н. Электроформование волокнистых материалов (ЭФВ-процесс). – М.: Нефть и газ, 1997. 231 с.

2. Петров А.В., Лукашевич А.Д., Бакеева И.В., Симонов-Емельянов И.Д., Филатов Ю.Н. Влияние молекулярной массы поли-N-винилпирролидона на получение ультратонких волокон методом электроформования из растворов // Вестник МИТХТ. 2011. Т. 6. №. С. 34–39.

3. Тагер А.А. Физико-химия полимеров. – М.: Научный мир, 2007. 576 с.

4. Vinogradov G.V., Malkin A.Ya., Blinova N.K., Srgeyenkov S.I., Zabugina M.P., Titkova L.V., Yanovsky Yu.G., Shalganova V.G. Peculiarities of flow and viscoelastic properties of solutions of polymers with a narrow molecular-weight distribution // Eur. Polymer J. 1973. V. 9. Р. 1231–1249.

5. Малкин А.Я., Исаев А.И. Реология: концепции, методы, приложения. – СПб.: ЦОП «Профессия», 2010. 560 с.

6. Shenoy S.L., Bates W.D., Frisch H.L., Wnek G.E. Role of chain entanglements on fiber formation during electrospinning of polymer solutions: good solvent, non-specific polymer-polymer interaction limit // Polymer. 2005. V. 46. Р. 3372–3384.

7. Son W.K., Youk J.H., Lee T.S., Park W.H. The effects of solution properties and polyelectrolyte on electrospinning of ultrafine poly(ethylene oxide) fibers // Polymer. 2004. V. 45. № 9. Р. 2959–2966.

8. Gupta P., Elkins C., Long T.E., Wilkes G.L. Electrospinning of linear homopolymers of poly-(methyl methacrylat): Exploring relationships between fiber formation, viscosity, molecular weight and concentration in good solvent // Polymer. 2005. V. 46. Р. 4799–4810.

9. Аскадский А.А., Кондращенко В.И. Компьютерное материаловедение полимеров. Т. 1. Атомно-молекулярный уровень. – М.: Научный мир, 1999. 544 с.